Superior Process Quality With Picosun's new R&D PEALD Technology
ESPOO, Finland, Aug. 29, 2019 /PRNewswire/ -- Picosun Group, the leading supplier of AGILE ALD® (Atomic Layer Deposition) thin film coating solutions, reports excellent results obtained with its next generation R&D PEALD (plasma-enhanced ALD) technology.
PEALD enables deposition at low temperatures and of several materials that could not be deposited with thermal process only. The drawback of PEALD, however, is damage to the sample surface, caused by ion bombardment. Picosun's solution to this is remote plasma method, where the plasma source is located high enough above the sample, and the reactive species hitting the surface are radicals, not high-energy ions.
"Picosun's operating philosophy is based on constant improvement and development, as we want to offer our customers always the best-in-class, leading quality ALD solutions. Our Picoplasma™ equipment has been a hit product in the R&D community since its launch, and we have now upgraded it to a completely new level, to enable even faster processing with superior film quality and purity," says Dr. Jani Kivioja, CTO of Picosun Group.
Picosun's next generation PEALD solution is based on remote, high power microwave plasma (MWP). The compact, lightweight plasma generator can be integrated to existing PICOSUN® R&D ALD reactors as such. The new plasma-ALD solution realizes deposition with virtually no added particles, with extremely low metal contamination and with far shorter cycle times compared to the previously used method. Excellent film quality and uniformity have been obtained(*), and the new MWP allows wider operating range (in terms of plasma parameters) which widens also the selection of available ALD processes.
"We are pleased to provide our customers with our new, thoroughly upgraded plasma-ALD solution. There are several important application areas, such as medical devices and MEMS, where substrates are sensitive and require processing at low temperatures. Now we have an ideal solution to this, which will again facilitate ALD's breakthrough to yet new components and devices," continues Dr. Kivioja.
(*) Film properties, SiO2 as an example:
Wafer size, dep. temperature, growth rate |
Film non-uniformity (1σ, 5mm EE, 49pts) |
Leakage current (@4MV) |
Particles (@>0,25µm) |
Metal contamination (Fe, Ti, Cr, Mn, Ni, Cu, Zn atoms) |
200 mm, 400 oC, 0.86 Å/cycle |
1.7 % (~10 nm film) |
2.1 x 10-8 A/cm2 |
< 60 |
< 2 x 1010 /cm2 |
Picosun provides the most advanced ALD thin film coating technology to enable the industrial leap into the future, with turn-key production solutions and unmatched expertise in the field. Today, PICOSUN™ ALD equipment are in daily manufacturing use in numerous major industries around the world. Picosun is based in Finland, with subsidiaries in Germany, North America, Singapore, Taiwan, China and Japan, offices in India and France, and a world-wide sales and support network. Visit www.picosun.com.
More information:
Dr. Jani Kivioja
CTO, Picosun Group
Tel: +358-46-922-8804
Email: info@picosun.com;
Web: www.picosun.com
This information was brought to you by Cision http://news.cision.com
The following files are available for download:
Share this article